Glass-ceramics bonding in geriatric patients: comparison with young teeth

The aim of the study was to assess whether in geriatric patients, the shear bond strength (SBS) of glass-ceramics differed when compared to young controls.

In the need of aesthetic restorations for geriatric patients, reliable bonding of glass-ceramics should be accomplished; however, glass-ceramics bonding on aged tooth structures is still unclear.

Sixty extracted molars from young and geriatric patients [18-25 (Y), and 65-80 (O)] were cut buccolingually to prepare enamel (E) and dentin (D) surfaces. Both surfaces were randomly divided into three groups according to the resin cements: Variolink II (V); Superbond (S); and Clearfil Esthetic Cement (C) (n = 10). Disc-shaped glass-ceramics (IPS E-max Press) (n = 120) were prepared. Specimens were bonded and subjected to thermocycling. SBS test was performed using a universal testing machine (0.5 mm/min). After debonding, the surfaces were examined using stereomicroscope and scanning electron microscope. Data were statistically analysed with Kolmogorov-Smirnov, Levene, anova and Bonferroni tests (p = 0.05).

There were no significant differences between the old and young teeth surfaces. V showed the highest SBS [MPa(SD)] on both enamel and dentin [36.7 (6.5) (YE), 23.2 (13.2) (YD), 32.1 (16.2) (OE), 25.5 (8.6) (OD), respectively]. Significant differences were observed between resin cements (p < 0.05). The failure types were 43% adhesive between tooth and cement, 48% mix, 9% adhesive between cement and ceramic, regardless of cement type.

In geriatric patients, the shear bond strength of glass-ceramics did not differ when compared to that of young controls. On the dentin surface, etch-rinse resin cements appear to be more appropriate for glass-ceramics bonding.