Pull-out retentive strength of fiber posts cemented at different times in canals obturated with a eugenol-based...

Currently, no standard luting protocol exists for fiber posts. In addition, no agreement has been reached on the time interval between canal obturation and post space preparation and cementation.

The purpose of this in vitro study was to evaluate the retention of fiber posts cemented with 3 different types of cement: Paracore, Variolink II, and RelyX Unicem cement after 24 hours or 2 weeks in root canals obturated with gutta percha and a eugenol-based sealer.

Seventy-two caries-free, freshly extracted, single-rooted human mandibular first premolar teeth with straight root canals were prepared and obturated with gutta percha and Endofil sealer. Specimens were divided into 2 groups (n=36): post spaces prepared 24 hours after obturation and post spaces prepared 2 weeks after obturation. Posts in both groups were luted with 1 of 3 different luting agents (n=12), ParaCore, Variolink II, or RelyX Unicem cement. Each tooth specimen was vertically secured in a universal testing machine, and a constant pull-out loading rate of 0.5 mm/min was applied until cement failure occurred. Data were statistically analyzed with 2-way and 1-way ANOVAs and t tests.

Two-way ANOVA indicated statistically significant differences in mean post retention among the 3 cement types (P<.001) and among the means of the different time intervals investigated (P<.001). Significant differences were noted among all cement types tested between the 24-hour and 2-week time intervals (P<.05).

Time elapsed between canal obturation and post cementation significantly influenced fiber post retention, regardless of the type of resin cement. Fiber posts showed significantly higher retention if cemented after 24 hours of obturation than if cementation occurred after 2 weeks.