Fracture load and failure types of different veneered polyetheretherketone fixed dental prostheses

Simon Taufall1, Marlis Eichberger1, Patrick R Schmidlin2

  • 1Department of Prosthodontics, Dental School, Ludwig-Maximilians-University Munich, Goethestrasse 70, 80336, Munich, Germany.

Clinical Oral Investigations
|March 17, 2016
PubMed
Abstract

Keywords:
Digital veneeringFracture loadPEEKVeneering resin composite

More Related Videos

Imaging of the Microstructural Failure Mechanism in the Human Hip08:43

Imaging of the Microstructural Failure Mechanism in the Human Hip

Published on: September 29, 2023

1.5K
In situ Compressive Loading and Correlative Noninvasive Imaging of the Bone-periodontal Ligament-tooth Fibrous Joint07:09

In situ Compressive Loading and Correlative Noninvasive Imaging of the Bone-periodontal Ligament-tooth Fibrous Joint

Published on: March 7, 2014

13.9K

Related Concept Videos

Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
994
Stress-Strain Diagram - Brittle Materials01:24

Stress-Strain Diagram - Brittle Materials

Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display...
4.9K
Behavior of Concrete Under Compressive Load01:23

Behavior of Concrete Under Compressive Load

Concrete exhibits specific behaviors under different compressive loads. Understanding this is crucial for understanding its structural integrity. When concrete undergoes uniaxial compression, it tends to develop cracks that run parallel to the direction of the force. These parallel cracks stem from localized tensile stresses that occur perpendicular to the compression direction. Additionally, angled cracks may appear due to the formation of shear planes.
As the concrete specimen fractures under...
784
Veneer01:19

Veneer

Veneer refers to a thin sheet of wood, typically produced to a thickness of about one-eighth of an inch or less. This material is crafted through various methods, the most common being rotary cutting. In this process, a log is mounted into a large lathe and spun against a knife edge, peeling off a continuous strip of wood as the knife penetrates deeper into the rotating log, creating a rotary-cut veneer.
Other veneering techniques include plain-slicing, quarter-slicing, and rift-slicing. These...
470
Plastic Deformations01:19

Plastic Deformations

Plastic deformation represents a fundamental concept in materials science, which explains the irreversible change in the shape of a material when it experiences stress beyond its elastic capability. This phenomenon is important in structural engineering, especially in designing and analyzing cantilever beams—structures that are securely fixed at one end and bear loads at the opposite end. When these beams are subjected to loads within their elastic range, they will return to their...
567
Fractures: Bone Repair01:27

Fractures: Bone Repair

Treatment for a fracture is based on the type of break, the bone affected, and the patient's age.
Minor fractures with no bone displacement are treated by immobilizing the fractured bone using a cast or splint. However, in the case of fractures with displaced bones, the broken bones are repositioned before immobilization to ensure successful healing without deformation and loss of function. The realignment of fractured bone ends is performed through a process called reduction. If the...
6.5K