Common Building Motifs in Ba2Fe3(PO4)4·2H2O, BaFe3(PO4)3, and Na3Fe3(PO4)4: Labile Fe(2+)/Fe(3+) Ordering and...

Two new mixed-valence Fe(2/3+) barium phosphates have been synthesized in hydrothermal conditions and characterized: Ba2Fe(2.66+)3(PO4)4·2H2O (compound 1, ratio Fe(3+)/Fe(2+) = 2:1, orthorhombic space group Pbca, a = 6.71240(10) Å, b = 10.6077(2) Å, c = 20.9975(5) Å, R1 = 3.39%) and BaFe(2.33+)3(PO4)3 (compound 2, ratio Fe(3+)/Fe(2+) = 1:2, orthorhombic, space group Imma with a = 10.5236(3) Å, b = 13.4454(4) Å, c = 6.6411(2) Å, R1 = 1.63%). 1 has a two-dimensional crystal structure built of [Fe(2.5+)2Fe(3+)1(PO4)4](4-) layers with charge segregation on two individual Fe crystal sites, in contrast to the single valence on these two sites found in similar layers of Na3Fe(3+)3(PO4)4. The crystal structure of 2 is formed of the same layers but condensed into a 3D [Fe(2+)2Fe(3+)1(PO4)3](2-) framework. The complete Fe(2+) vs Fe(3+) charge ordering on the two available sites differs from what was found in the two previous cases and denotes a remarkable charge adaptability of the common elementary units. Compared to the antiferromagnetic Na3Fe(3+)3(PO4)4 the partial iron reduction into Fe(2+) is responsible for strong ferromagnetic components along the c-easy axis for both 1 and 2. Additionally 1 shows multiple magnetization steps in the perpendicular direction, giving raise to atypical anisotropic magnetism into a complex magnetic phase diagram.