New Water Vapor Barrier Film Based on Lamellar Aliphatic-Monoamine-Bridged Polysilsesquioxane

Siloxane-based hybrid lamellar materials with ordered nanostructure units paralleling to the substrate have been widely used for water vapor barrier. However, it is very difficult to control the orientation of the lamellar units at molecular level. In this Research Article, a new lamellar bridged polysilsesquioxane (BPSQ) film, whose voids between lamellae were filled by pendant alkyl chains in the organic bridge, was prepared via the stoichiometric reaction between 3-glycidoxypropyltrimethoxysilane and aliphatic monoamine at 60 °C without catalyst. Experimental evidence obtained from FT-IR, MS, NMR, and GIXRD techniques suggested that the as-prepared BPSQ films were constructed by lamellar units with disordered orientation. Nonetheless, they possessed satisfactory water vapor barrier performance for potassium dihydrogen phosphate (KDP) and deuterated potassium dihydrogen phosphate (DKDP) optical crystals, and the water vapor transmission rate through BPSQ film with thickness of 25 μm was as low as 20.3 g·m(-2)·d(-1). Those results proved that filling the voids between molecular lamellae with alkyl chains greatly weakened the effect of lamellar unit orientation on the vapor barrier property of BPSQ film.