Tear and decohesion of bovine pericardial tissue

The aim of this study was to evaluate quantitatively the fracture-by tear and delamination-of bovine pericardium tissues which are usually employed for the manufacture of bioprosthetic valves. A large number of samples (77) were tested in root-to-apex and circumferential directions, according to a standardised tear test (ASTM D 1938). Before performing the tear test, some samples were subjected to 1000 cycles of fatigue to a maximum stress of 3MPa. Fracture toughness of tearing and delamination were computed by following a simple fracture model. The study showed significantly lower values of delamination toughness compared with tear delamination. Moreover, tear forces were different in each test direction, revealing a clear orthotropic behaviour. All these results, as well as the testing procedure, could be of value for future research in the physiological function of pericardium tissues and clinical applications.