Out-of-Plane Magnetic Moment and Lattice Distortion in Sputtered Ge Added Fe3O4 Thin Film

Fe3O4 has been known to have attractive physical properties for spintronic applications such as half-metallicity, however, its complicated magnetism has yet to be elucidated fully. We investigated the sputtered polycrystalline Fe3O4 thin film in which Ge was added for stabilization of the spinal structure. From X-ray photoelectron and Raman spectroscopies, major part of added Ge is found to be quadrivalent and considered to be incorporated in the spinel structure. Out-of-plane alignment of the local moment was confirmed by conversion electron Mössbauer spectroscopy and magnetization measurements with an applied field up to 70 kOe also support it. The Pawley refinement of the X-ray diffraction profile with a series of possible space groups in the spinel structure suggests that the crystal symmetry is reduced from cubic to tetragonal or orthorhombic spinels with (100) or (010) strains up to -0.231%. The uniaxial anisotropy constants K(u) for the tetragonally distorted cases estimated from the evaluated strains and the ab-initio calculation were found to be around 1.05 x 10(6) erg/cm3. We consider that the magnetic anisotropy induced by the lattice distortion contributes to the out-of-plane alignment of local moments in addition to the previously reported effect by the exchange coupling across crystallographic defects of the antiphase boundaries.