Combined Embedding of N/F-Doping and CaCO3 Surface Modification in the TiO2 Photoanode for Dye-Sensitized Solar Cells

N/F-doping and CaCO3 surface modification was carried out in TiO2 photoelectrodes for dye-sensitized solar cells (DSSCs). The combined effect of the N/F doped TiO2 and the CaCO3 coating showed a great increase of the short-circuit current (J(sc)), and photoelectric conversion efficiency (η) of the prepared cells; the efficiency (η) was improved from 7.00% of a commercial TiO2 photoelectrode to 7.90% of an uncoated N/F-doped electrode, and to 9.09% of a N/F-doped and CaCO3 surface modified electrode. An enhanced photoresponse in N/F-doped TiO2 nanoparticles generate more photo-excited electrons, as supported by measured UV-Vis diffuse reflectance spectra. A successive CaCO3 surface modification then forms a barrier on the surface of the N/F-doped TiO2 particles; the higher basicity of the CaCO3 modified TiO2 facilitates the dye adsorption, as supported by the direct measurement of the amount of adsorbed dye.