Effects of Temperature and Pore Structure on High Surface Area-Activated Carbon Obtained from Peanut Shells

Activated carbon was synthesized from peanut shells by treating with H3PO4 with an intention to enhance the surface area and to find its electrochemical performance in EDLC as electrode material. The powdered peanut shells were pyrolyzed at three different temperatures namely 300 degrees C, 600 degrees C and 800 degrees C respectively. The structural and surface properties of the pyrolyzed carbon materials were studied using N2 adsorption/desorption, Raman, TEM and SEM analysis. There has been remarkable increase in the surface area of the carbon pyrolyzed at 600 degrees C due to the effect of pore generations. The surface area of the 600 degrees C pyrolyzed sample was found to be 1629 m2/g. The electrochemical properties of all the samples were evaluated by cyclic voltammetry, impedance spectroscopy, and galvanostatic charge-discharge tests. The system showed excellent cycleability and a maximum specific capacitance of 291 Fg(-1) was obtained in a 0.1 M H2SO4 electrolyte solution. The effects of the various properties of the activated carbon on the EDLC performance are discussed.