Preparation and Characterization of Nanostructured Manganese Oxide for Supercapacitors

Nanostructured manganese oxides were synthesized by a sol-gel method using manganese acetate (MnAc2) and citric acid (C6H8O7,) as precursors, and characterized by Brunauer-Emmett-Teller (BET) analysis, Barrett-Joyner-Halenda (BJH), X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM) techniques. The nano-rod structure of MnO2 developed gradually when the calcination temperature varied from 380 to 580 degrees C. As the pH increased, the pore size increased, while the specific surface area decreased. The effects of the pH and calcination temperature on the electrochemical properties of the nano-MnO2 electrode, including the supercapacitive behavior, were investigated by cyclic voltammetry (CV) tests. The tests were performed between 0 and 0.8 V versus Ag/AgCl in 1 M Na2SO4 electrolyte at various scan rates (10-200 mVs(-1)). The specific capacitance of the SP-380 sample, prepared at pH 6, was equal to 269.3 Fg(-1). After 300 cycles, approximately a 3.4% increase of the specific capacitance was measured, confirming the excellent cyclability.