Cavitation-Induced Fracture Causes Nanocorrugations in Brittle Metallic Glasses

I Singh1, R Narasimhan1, Upadrasta Ramamurty2

  • 1Department of Mechanical Engineering, Indian Institute of Science, Bangalore 560012, India.

Physical Review Letters
|August 6, 2016
PubMed

More Related Videos

Determining the Mechanical Strength of Ultra-Fine-Grained Metals05:04

Determining the Mechanical Strength of Ultra-Fine-Grained Metals

Published on: November 22, 2021

2.7K
Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

929

Related Concept Videos

Stress-Strain Diagram - Brittle Materials01:24

Stress-Strain Diagram - Brittle Materials

Brittle materials, including glass, cast iron, and stone, exhibit unique characteristics. They fracture without considerable change in their elongation rate, indicating that their breaking and ultimate strength are equivalent. Such materials also show lower strain levels at the point of rupture. The failure in brittle materials predominantly results from normal stresses, as evidenced by the rupture created along a surface perpendicular to the applied load. These materials do not display...
4.8K
Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
975
Imperfections in Crystal Structure: Point, Line and Plane Defects01:25

Imperfections in Crystal Structure: Point, Line and Plane Defects

A perfect crystal, in theory, has a uniform structure with the same unit cell and lattice points throughout. However, any deviation from this periodic arrangement is known as an imperfection or defect. These defects can be categorized into three types: point, line, and plane defects.Point defects occur when there is a deviation from the ideal due to missing atoms, displaced atoms, or additional atoms. These imperfections might occur due to imperfect packing during crystallization or because of...
40
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
528
Imperfections in Crystal Structure: Non-Stoichiometric Defects01:29

Imperfections in Crystal Structure: Non-Stoichiometric Defects

Non-stoichiometric defects refer to a type of defect in the crystal structure of a compound where the ratio of its constituent elements deviates from the ideal stoichiometric ratio. There are two main types of non-stoichiometric defects: metal excess defects and metal deficiency defects.Metal excess defects occur when there is a slight surplus of metal ions than what is required by the stoichiometric ratio of the compound. For example, heating a sodium chloride crystal in sodium vapor results...
31