Chemical Synthesis of Porous Barium Titanate Thin Film and Thermal Stabilization of Ferroelectric Phase by Porosity-Induced Strain
Published on: March 27, 2018
Piezoelectric and Dielectric Properties of Multilayered BaTiO3/(Ba,Ca)TiO3/CaTiO3 Thin Films
Xiao Na Zhu1,2, Ting Ting Gao1, Xing Xu2
1Laboratory of Dielectric Materials, School of Materials Science and Engineering, Zhejiang University , Hangzhou 310027, China.
Abstract:
Highly oriented multilayered BaTiO3-(Ba,Ca)TiO3-CaTiO3 thin films were fabricated on Nb-doped (001) SrTiO3 (Nb:STO) substrates by pulsed laser deposition. The configurations of multilayered BaTiO3-(Ba,Ca)TiO3-CaTiO3 thin films are designed with the thickness ratio of 1:1:1 and 2:1:1 and total thickness ∼300 nm. Microstructural characterization by X-ray diffraction indicates that the as-deposited thin films are highly c-axis oriented and large in-plane strain is determined in BaTiO3 and CaTiO3 layers. Piezoresponse force microscopy (PFM) studies reveal an intense in-plane polarization component, whereas the out-of-plane shows inferior phase contrast. The optimized combination is found to be the BaTiO3-(Ba0.85Ca0.15)TiO3-CaTiO3 structure with combination ratio 2:1:1, which displays the largest domain switching amplitude under DC electric field, the largest room-temperature dielectric constant ∼646, a small dielectric loss of 0.03, and the largest dielectric tunability of ∼50% at 400 kV/cm. These results suggest that the enhanced dielectric and tunability performance are greatly associated with the large in-plane polarization component and domain switching.