Design and synthesis of an amphiphilic graft hydrogel having a hydrophobic domain formed by multiple interactions

A novel hydrogel having hydrophobic oligo segments and hydrophilic poly(acrylamidoglycolic acid) (PAGA) as pH responsive polymer segments was designed and synthesized to be used as a soft biomaterial. Poly(trimethylene carbonate) (PTMC) as the side chain, for which the degrees of polymerization were 9, 19, and 49, and the composition ratios were 1, 5, and 10mol%, was used as the oligo segment in the hydrogel. The swelling ratio of the hydrogel was investigated under various changes in conditions such as pH, temperature, and hydrogen bonding upon urea addition. Under pH2-11 conditions, the graft gel reversibly swelled and shrank due to the effect of PAGA main chain. The interior morphology and skin layer of the hydrogel was observed by a scanning electron microscope. The hydrogel composed of PAGA as the hydrophilic polymer backbone had a sponge-like structure, with a pore size of approximately 100μm. On the other hand, upon increasing the ratio of trimethylene carbonate (TMC) units in the hydrogel, the pores became smaller or disappeared. Moreover, thickness of the skin layer significantly increased with the swelling ratio depended on the incorporation ratios of the PTMC macromonomer. Molecular incorporation in the hydrogel was evaluated using a dye as a model drug molecule. These features would play an important role in drug loading. Increasing the ratio of TMC units favored the adsorption of the dye and activation of the incorporation behavior.