Selected physical properties of new resin-modified glass ionomer luting cements

Two resin-modified glass ionomer (RMGI)-based luting agents have been recently marketed without independent reports of their physical properties.

The purpose of this in vitro study was to evaluate selected physical properties of 2 newly marketed RMGI luting agents and compare the findings with traditional materials.

Specimens (N=12) of Nexus RMGI, UltraCem, GC Fuji Cem 2, and RelyX Luting Plus were fabricated using standardized molds for flexural strength and fracture toughness according to manufacturer recommendations and stored in physiologic phosphate-buffered saline solution at 37°C until testing. Specimens were tested at 1 and 24 hours, 1 week, and 1 month. Mean values for flexural strength, flexural modulus, flexural toughness, and fracture toughness were determined. Additionally, film thickness (N=12) for each material was determined following Amerian National Standards Association/American Dental Association (ANSI/ADA) specifications. Mean results were analyzed with Kruskal-Wallis and Mann-Whitney U tests (α=.05).

All luting agents exhibited a similar film thickness that met ANSI/ADA requirements for aqueous-based luting agents. Nexus RMGI surprisingly demonstrated significantly greater flexural strength and fracture toughness at 1 hour, which decreased significantly at 24 hours, making it similar to the other materials evaluated. All materials had similar flexural strength values at 7 days.

Physical property performance was material dependent. Nexus RMGI demonstrated greater early physical properties that were significantly less at 24 hours. UltraCem, GC Fuji Cem 2, and RelyX Luting Plus demonstrated the increasing physical property development that is normally associated with polyalkenoate-based systems.