Characterization of Polyester Cloth as an Alternative Separator to Nafion Membrane in Microbial Fuel Cells for...

Polyester cloth (PC) was selected as a prospective inexpensive substitute separator material for microbial fuel cells (MFCs). PC was compared with a traditional Nafion proton exchange membrane (PEM) as an MFC separator by analyzing its physical and electrochemical properties. A single layer of PC showed higher mass transfer (e.g., for O₂/H⁺/ions) than the Nafion PEM; in the case of oxygen mass transfer coefficient (k_o), a rate of 50.0 × 10⁻⁵ cm·s⁻¹ was observed compared with a rate of 20.8 × 10⁻⁵ cm/s in the Nafion PEM. Increased numbers of PC layers were found to reduce the oxygen mass transfer coefficient. In addition, the diffusion coefficient of oxygen (D_O) for PC (2.0-3.3 × 10⁻⁶ cm²/s) was lower than that of the Nafion PEM (3.8 × 10⁻⁶ cm²/s). The PC was found to have a low ohmic resistance (0.29-0.38 Ω) in the MFC, which was similar to that of Nafion PEM (0.31 Ω); this resulted in comparable maximum power density and maximum current density in MFCs with PC and those with Nafion PEMs. Moreover, a higher average current generation was observed in MFCs with PC (104.3 ± 15.3 A/m³) compared with MFCs with Nafion PEM (100.4 ± 17.7 A/m³), as well as showing insignificant degradation of the PC surface, during 177 days of use in swine wastewater. These results suggest that PC separators could serve as a low-cost alternative to Nafion PEMs for construction of cost-effective MFCs.