Related Experiment Video

Updated: Mar 14, 2026

Evaluation of the Curing of Adhesive Systems by Rheological and Thermal Testing
09:06

Evaluation of the Curing of Adhesive Systems by Rheological and Thermal Testing

Published on: July 3, 2020

7.8K

Shear bond strength of a novel light cured calcium silicate based-cement to resin composite using different adhesive

Hanan Alzraikat1, Nessrin A Taha, Deema Qasrawi

  • 1Department of Conservative Dentistry, Jordan University of Science and Technology.

Dental Materials Journal
|September 30, 2016
PubMed

More Related Videos

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material07:42

Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material

Published on: December 20, 2024

926
Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation08:45

Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation

Published on: July 21, 2014

14.1K

Related Concept Videos

Bonding and Strength of Aggregate01:12

Bonding and Strength of Aggregate

The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
548
Strength of Cement01:20

Strength of Cement

Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
712
Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
1.2K
Aggregate Cement Ratio01:21

Aggregate Cement Ratio

The Aggregate Cement ratio refers to the weight of aggregate divided by the weight of cement in a concrete mix. Altering this ratio has profound effects on the concrete's properties. This ratio plays a pivotal role in determining the strength, workability, and durability of concrete. When the Aggregate Cement ratio is higher, the mix is leaner, meaning it has less cement paste to lubricate the aggregate, potentially making the concrete less workable. Such mixes, known as lean, enhance the...
625
Accelerators01:17

Accelerators

Accelerators in concrete serve as admixtures to speed up the hardening process, enabling the concrete to achieve early strength faster. Although accelerators do not necessarily impact the time it takes concrete to set, they reduce this time in practice. A common accelerator is calcium chloride, which is particularly useful for hastening early strength development in cold weather or for rapid repair jobs that require quick heat generation after mixing.
The effectiveness of calcium chloride can...
325
Tensile Strength Considerations of Concrete01:16

Tensile Strength Considerations of Concrete

Considering the tensile strength of concrete involves recognizing that the theoretical strength of cement paste can be up to a thousand times higher than what is observed in practical applications. This significant discrepancy is largely attributed to the presence of microscopic cracks within the concrete. These cracks tend to amplify stress at their tips when a load is applied, a phenomenon explained by Griffith's theory of brittle fracture.
The dimensions and shape of a concrete specimen...
706