Blue-Light Transmittance of Esthetic Monolithic CAD/CAM Materials With Respect to Their Composition, Thickness, and...

Determining the amount of blue light (360-540nm) passing through nine monolithic computer-aided design/computer-aided manufacturing (CAD/CAM) materials depends on material thickness, initial irradiance, and the distance between the curing unit and the specimen's surface. A total of 180 specimens of two thicknesses (1 mm and 2 mm, n=10/subgroup) were fabricated from TelioCAD, VITA CAD-Temp (VCT), experimental nanocomposite, LAVA Ultimate (LU), VITA ENAMIC (VE), VITA MarkII (VM), IPS EmpressCAD (IEC), IPS e.maxCAD (IEM), and CELTRA DUO (CD). The irradiance passing through the CAD/CAM materials and thicknesses was measured using a light-emitting-diode curing unit with standard-power, high-power, and plasma modes by means of a USB4000 spectrometer. The curing unit was placed directly on the specimen's surface at 2- and 4-mm distances from the specimen's surface. Data were analyzed using a multivariate analysis and one-way analysis of variance with the post hoc Scheffé test (p<0.05). The highest transmitted irradiance was measured for VM and LU, followed by VCT and IEC, while the lowest values showed VE, followed by IEM and CD. The highest transmitted irradiance was recorded by exposing the material to the plasma mode, followed by the high- and standard-power modes. The measured irradiance was decreased by increasing the specimen's thickness from 1 to 2 mm. Fewer differences were measured when the curing unit was placed at 0 or 2 mm from the specimen's surface, and the irradiance passing through the specimens was lower at a distance of 4 mm.