Significant shear bond strength improvements of a resin-modified glass ionomer cement with a resin coating

Michael T Stallings, Daniel C Stoeckel, Kenneth G Rawson

    General Dentistry
    |January 10, 2017
    PubMed

    Keywords:
    glass ionomer cementresin coatingresin-modified glass ionomer cementresin-modified glass ionomer cementshear bond strengthdental restoration materialsresin coatingdental material durability

    More Related Videos

    Author Spotlight: Enhancing Fiber Composite Laminate Quality with the Wet Hand Lay-Up/Vacuum Bag Process09:54

    Author Spotlight: Enhancing Fiber Composite Laminate Quality with the Wet Hand Lay-Up/Vacuum Bag Process

    Published on: June 30, 2023

    3.3K
    Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation08:45

    Shrinkage of Dental Composite in Simulated Cavity Measured with Digital Image Correlation

    Published on: July 21, 2014

    14.1K

    Related Concept Videos

    Bonding and Strength of Aggregate01:12

    Bonding and Strength of Aggregate

    The bond between aggregate particles and the cement matrix is significantly influenced by the shape and surface texture of the aggregates. High-strength concretes benefit from a rougher texture, which leads to stronger bonding due to greater adhesion. Angular aggregates with larger surface areas also enhance this bond. The bonding quality, however, is complex to assess as no universally accepted test exists. Good bonding is indicated when a crushed concrete specimen shows some aggregate...
    545
    Fiber Reinforced Concrete01:22

    Fiber Reinforced Concrete

    Fiber-reinforced concrete significantly enhances the structural and nonstructural properties of traditional concrete by incorporating fibers like steel, glass, and polymers. These fibers, varying from natural ones such as sisal and cellulose to manufactured ones like polypropylene and Kevlar, are mixed into hydraulic cement with aggregates. Steel fibers, often preferred for their robustness, contribute to improved ductility, toughness, and post-cracking performance. The concrete is classified...
    474
    Accelerated Curing of Concrete01:25

    Accelerated Curing of Concrete

    Accelerating concrete curing is achieved by applying heat and additional moisture. This process accelerates the hydration of the cement, resulting in an earlier strength gain in the concrete. Steam curing is a method wherein the concrete products are either transported through a chamber on a conveyor belt or encased in plastic, allowing steam at atmospheric pressure to circulate freely around them. This process begins with a phase of moist curing that typically lasts between 3 to 5 hours, after...
    530
    Mortar Properties01:17

    Mortar Properties

    Mortar properties encompass a range of characteristics crucial for construction and masonry work, including workability, water retention, bond strength, durability, compressive strength, volume change, and appearance. Workability refers to mortar's ability to be easily applied and manipulated without sagging or falling off surfaces, which is important for efficient masonry unit placement and alignment. Water retention is essential to prevent the mortar from losing moisture too quickly to...
    540
    Strength of Cement01:20

    Strength of Cement

    Strength tests for cement are not performed directly on neat cement paste due to difficulty in obtaining consistent, reliable specimens. Instead, cement is typically tested in the form of cement-sand mortar.
    For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...
    699