Surface Functionalization of Metal-Organic Frameworks for Improved Moisture Resistance
Published on: September 5, 2018
Imparting surface hydrophobicity to metal-organic frameworks using a facile solution-immersion process to enhance
Xukun Qian1, Fuxing Sun2, Jing Sun3
1School of Engineering, Lishui University, Lishui 323000, P.R. China. qianxukun@126.com and State Key Laboratory of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, 1295 Dingxi Road, Shanghai 200050, P.R. China.
Abstract:
The water sensitivity of metal-organic frameworks (MOFs) poses a critical issue for their large-scale applications. One effective method to solve this is to provide MOFs with a hydrophobic surface. Herein, we develop a facile solution-immersion process to deposit a hydrophobic coating on the MOFs' external surface without blocking their intrinsic pores. The water contact angle of the surface hydrophobic (SH) MOFs is ∼146°. The hydrophobic coating not only greatly enhances MOFs' water stability but also provides durable protection against the attack of water molecules. When exposed to liquid water, the SH samples well retain their crystal structure, morphology, surface area and CO2 uptake capacity. However, the as-synthesized (AS) samples nearly collapse and lose their porosity as well as CO2 uptake capacity after the same exposure. This study opens up a new avenue for the MOFs' application of gas sorption in the presence of water.