Production and characterization of medium-chain-length polyhydroxyalkanoate copolymer from Arctic psychrotrophic...

Arctic psychrotrophic bacterium Pseudomonas sp. PAMC 28620 was found to produce a distinctive medium-chain-length polyhydroxyalkanoate (MCL-PHA) copolymer when grown on structurally unrelated carbon sources including glycerol. The maximum MCL-PHA copolymer yield was obtained about 52.18±4.12% from 7.95±0.66g/L of biomass at 144h of fermentation when 3% glycerol was used as sole carbon and energy source during the laboratory-scale bioreactor process. Characterization of the copolymer was carried out using fourier transform infrared spectroscopy (FTIR), gas chromatography-mass spectrometry (GC-MS), proton (¹H) and carbon (¹³C) nuclear magnetic resonance spectroscopy (NMR), gel permeation chromatography (GPC), differential scanning calorimeter (DSC) and thermo-gravimetric analysis (TGA). The copolymer produced by Pseudomonas sp. PAMC 28620 consisting of four PHA monomers and identified as 3-hydroxyoctanoate (3HO), 3-hydroxydecanoate (3HD), 3-hydroxydodecanoate (3HDD) and 3-hydroxytetradecanoate (3HTD). An average molecular weight of the copolymer was found approximately 30.244kDa with polydispersity index (PDI) value of 2.05. Thermal analysis showed the produced MCL-PHA copolymer to be low-crystalline (43.73%) polymer with great thermal stability, having the thermal decomposition temperature of 230°C-280°C, endothermic melting temperature (T_m) of 172.84°C, glass transition (T_g) temperature of 3.99°C, and apparent melting enthalpy fusion (ΔH_m) about 63.85Jg^-1.