The effect of Sr(OH)2 on the hydrogen storage properties of the Mg(NH2)2-2LiH system
Hujun Cao1, Han Wang2, Claudio Pistidda1
1Institute of Materials Research, Materials Technology, Helmholtz-Zentrum Geesthacht GmbH, Max-Planck-Straße 1, D-21502 Geesthacht, Germany. hujun.cao@hzg.de.
Abstract:
The doping effect of Sr(OH)2 on the Mg(NH2)2-2LiH system is investigated considering different amounts of added Sr(OH)2 in the range of 0.05 to 0.2 mol. Experimental results show that both the thermodynamic and the kinetic properties of Mg(NH2)2-2LiH are influenced by the presence of Sr(OH)2. The addition of 0.1 mol Sr(OH)2 leads to a decrease in both the dehydrogenation onset and peak temperatures of ca. 70 and 13 °C, respectively, and an acceleration in the de/re-hydrogenation rates of one time at 150 °C compared to Mg(NH2)2-2LiH alone. Based on differential scanning calorimetry (DSC) analysis, the overall reaction enthalpy of the 0.1 Sr(OH)2-doped sample is calculated to be 44 kJ per mol-H2 and there are two absorption events occurring in the doped sample instead of one in the pristine sample. For the applied experimental conditions, according to the in situ synchrotron radiation powder X-ray diffraction (SR-PXD) and Fourier Transform Infrared spectroscopy (FT-IR) analysis, the reaction mechanism has been finally defined: Sr(OH)2, Mg(NH2)2 and LiH react with each other to form SrO, MgO and LiNH2 during ball milling. After heating, SrO interacts with Mg(NH2)2 producing MgO and Sr(NH2)2. Then Mg(NH2)2, LiNH2 and Sr(NH2)2 react with LiH to produce Li2NH, SrNH, Li2Mg(NH)2 and Li2Mg2(NH)3 in traces. After re-hydrogenation, LiSrH3, LiH and LiNH2 are formed along with amorphous Mg(NH2)2. The reasons for the improved kinetics are: (a) during dehydrogenation, the in situ formation of SrNH appears to increase the interfacial contacts between Mg(NH2)2 and LiH and also weakens the N-H bond of Mg(NH2)2; (b) during absorption, the formation of LiSrH3 at around 150 °C could be the key factor for improving the hydrogenation properties.
Related Concept Videos
01:19Acid Halides to Alcohols: LiAlH4 Reduction
The mechanism proceeds in three steps. First, the nucleophilic hydride ion attacks the carbonyl carbon of the acid halide to form a tetrahedral intermediate. Next, the carbonyl group is re-formed, and the halide ion departs as a leaving group, generating an aldehyde. A second nucleophilic attack by the hydride yields an alkoxide ion, which, upon protonation, gives a primary alcohol as...
00:55Nitriles to Amines: LiAlH4 Reduction
As shown below, the mechanism involves three steps. Firstly, the hydride ion acting as a nucleophile attacks the nitrile carbon to form an anion. In the second step, a second equivalent of the hydride ion attacks the anion to...
02:23Alcohols from Carbonyl Compounds: Reduction
Catalytic hydrogenation is similar to the reduction of an alkene or alkyne by adding H2 across the pi bond in the presence of transition metal catalysts like Raney Ni, Pd–C, Pt, or Ru. Aldehydes and ketones can be reduced by this method, often under mild to moderate heat (25–100°C) and...
01:20Amides to Amines: LiAlH4 Reduction
Amide reduction requires two equivalents of the reducing agent, acting as a source of hydride ions. As shown in the figure, the reaction is initiated with a nucleophilic attack by the hydride ion at the carbonyl carbon to form a tetrahedral intermediate.
01:17Esters to Alcohols: Hydride Reductions
Lithium aluminum hydride is a source of hydride ions and functions as a nucleophile. The mechanism proceeds in three steps. Firstly, the nucleophilic hydride ion attacks the carbonyl carbon of the ester to form a tetrahedral intermediate. Subsequently, the carbonyl group re-forms,...
03:12Chemical Stoichiometry and Gases: Using Ideal Gas Law to Determine Moles