Influence of Si substitution on the reactivity of α-tricalcium phosphate

Silicon substituted calcium phosphates have been widely studied over the last ten years due to their enhanced osteogenic properties. Notwithstanding, the role of silicon on α-TCP reactivity is not clear yet. Therefore, the aim of this work was to evaluate the reactivity and the properties of Si-α-TCP in comparison to α-TCP. Precursor powders have similar properties regarding purity, particle size distribution and specific surface area, which allowed a better comparison of the Si effects on their reactivity and cements properties. Both Si-α-TCP and α-TCP hydrolyzed to a calcium-deficient hydroxyapatite when mixed with water but their conversion rates were different. Si-α-TCP exhibited a slower setting rate than α-TCP, i.e. k_SSA for Si-TCP (0.021g·m^-2·h^-1) was almost four times lower than for α-TCP (0.072g·m^-2·h^-1). On the other hand, the compressive strength of the CPC resulting from fully reacted Si-α-TCP was significantly higher (12.80±0.38MPa) than that of α-TCP (11.44±0.54MPa), due to the smaller size of the entangled precipitated apatite crystals.