Enhancing the thermal dissipation of a light-converting composite for quantum dot-based white light-emitting diodes
Huai Zheng1,2, Xiang Lei3, Ting Cheng1
1Hubei Key Laboratory of Waterjet Theory and New Technology, School of Power and Mechanical Engineering, Wuhan University, Wuhan 430072, People's Republic of China.
Abstract:
Quantum dots (QDs) have been developed as one of the most promising light-converting materials for white light-emitting diodes (LEDs). In current QD-based LED packaging structures, composites of QDs and polymers are used as light-converting layers. However, the ultralow thermal conductivity of such composites seriously hinders the dissipation of QD-generating heat. In this paper, we demonstrate a method to enhance the thermal dissipation of QD-polymer composites through electrospinning polymer nanofibers. QD-polymer films embedded by electrospun nanofibers were prepared. Benefitting from aligned polymer chains in the electrospun nanofibers, the through-panel and in-panel thermal conductivities of the proposed QD-polymer film increased by 39.9% and 423.1%, respectively, compared to traditional QD-polymer film. The proposed and traditional QD-polymer films were both packaged on chip on board (CoB) LEDs for experimental comparison. Compared to traditional QD-polymer film, the luminous flux and luminous efficiency of the LEDs were increased by up to 51.8% and 42.9% by the proposed QD-polymer film under a current of 800 mA, respectively. With an increase in the driving current from 20-800 mA, the correlated color temperature (CCT) variation decreased by 72.7%. The maximum temperatures in the QD-polymer films were reduced from 419 K-411 K under a driving current of 200 mA.