Dendrimer-functionalized electrospun nanofibres as dual-action water treatment membranes

This work reports the preparation of composite electrospun membranes combining antimicrobial action with the capacity of retaining low-molecular weight non-polar pollutants. The membranes were electrospun blends of polyvinyl alcohol (PVA) and poly(acrylic acid) (PAA) stabilized using heat curing. The membranes were functionalized by grafting amino-terminated poly(amidoamine) (PAMAM) G3 dendrimers. The antimicrobial effect was assessed using strains of Escherichia coli and Staphylococcus aureus by tracking their capacity to form new colonies and their metabolic impairment upon contact with membranes. The antimicrobial activity was particularly high to the gram-positive bacterium S. aureus with a 3-log reduction in their capacity to colonize dendrimer-functionalized membranes with respect to neat PVA/PAA fibers. The effect to gram-positive bacteria was attributed to the interaction of dendrimers with the negatively charged bacterial membranes and resulted in membranes essentially free of bacterial colonization after 20h in contact with cultures at 36°C. The adsorption of toluene on PAA/PVA fibers and on dendrimer-functionalized membranes was assayed using toluene over a broad concentration range. The host-guest encapsulation of toluene inside dendrimer molecules was computed through docking studies, which allowed calculating a maximum capacity of 14 molecules of toluene per molecule of PAMAM G3. The theoretical prediction was in good agreement with the experimental capacity at the higher concentrations assayed.