Synthesis of CaCO3 nano- and micro-particles by dry ice carbonation
F C Donnelly1, F Purcell-Milton, V Framont
1School of Chemistry, Trinity College Dublin, Dublin 2, Ireland. igounko@tcd.ie.
Chemical Communications (Cambridge, England)
|June 7, 2017
Abstract:
Here we report a new low temperature dry ice carbonation approach for the synthesis of carbonate-based nano- and micro-particulate materials, which enables the preparation of monodispersed calcium carbonate nanoparticles and microspheres with very high purity phases.
Related Concept Videos
01:24Carbonation Shrinkage
519
Atmospheric CO2 penetrates the concrete's pores and, in the presence of moisture, forms carbonic acid, which then reacts with calcium hydroxide in the hydrated cement, forming calcium carbonate. This process reduces the concrete's volume and is termed carbonation shrinkage.
The concrete's permeability is slightly reduced as calcium carbonate produced during the reaction fills its pores. Furthermore, its strength is slightly enhanced as the water released during the reaction...
The concrete's permeability is slightly reduced as calcium carbonate produced during the reaction fills its pores. Furthermore, its strength is slightly enhanced as the water released during the reaction...
519
01:09Colloidal precipitates
6.6K
The high insolubility of some precipitates can result in an unfavorable relative supersaturation. This can lead to colloidal particles with a large surface-to-mass ratio, where adsorption is promoted. For instance, in the precipitation of silver chloride, silver ions are adsorbed on the surface of the colloidal particles, forming a primary layer. This layer attracts ions of opposite charge (such as nitrate ions), forming a diffuse secondary layer of adsorbed ions. This electric double layer...
6.6K