Fretting Fatigue with Cylindrical-On-Flat Contact: Crack Nucleation, Crack Path and Fatigue Life

Nitikorn Noraphaiphipaksa1, Anchalee Manonukul2, Chaosuan Kanchanomai3

  • 1Center of Materials Engineering and Performance, Department of Mechanical Engineering, Faculty of Engineering, Thammasat University, Pathumthani 12120, Thailand. nitikorn@engr.tu.ac.th.

Materials (Basel, Switzerland)
|August 5, 2017
PubMed

Keywords:
crack closurecrack nucleationcylindrical-on-flat contactfatigue lifefretting fatigue

More Related Videos

Crack Monitoring in Resonance Fatigue Testing of Welded Specimens Using Digital Image Correlation05:30

Crack Monitoring in Resonance Fatigue Testing of Welded Specimens Using Digital Image Correlation

Published on: September 29, 2019

8.7K
Ultrasonic Fatigue Testing in the Tension-Compression Mode06:54

Ultrasonic Fatigue Testing in the Tension-Compression Mode

Published on: March 7, 2018

11.2K

Related Concept Videos

Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
888
Stress Concentrations in Circular Shafts01:18

Stress Concentrations in Circular Shafts

Consider the elastic torsion formula, which applies to a circular shaft with a consistent cross-section. This formula assumes that the shaft's ends are loaded with rigid plates firmly attached. However, in many cases, torques are applied to the shaft through mechanisms like flange couplings or gears, which are connected by keys inserted into keyways. This application method modifies the stress distribution near the point of torque application, causing it to deviate from the distributions...
599
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
512
Stress Concentrations01:24

Stress Concentrations

Stress concentration is when stress intensifies near discontinuities such as holes or abrupt cross-sectional changes in a structural member. This localized stress can often surpass the average stress within the member. The stress distribution in flat bars, either with a circular hole or varying widths connected by fillets, can be determined experimentally using a photoelastic method. The results are based on ratios of geometric parameters like the ratio of the hole's radius to the smaller...
743
Stress Concentrations01:13

Stress Concentrations

The concept of stress concentration is crucial for understanding how materials respond under bending stresses, particularly when there are irregularities or discontinuities in the material's geometry. Normally, stress in a symmetric member subjected to pure bending is assumed to be uniformly distributed across the entire cross-section. However, this assumption does not hold when there are variations in the cross-sectional geometry or the presence of notches and holes.
The stress...
708
Fatigue Strength of Concrete01:22

Fatigue Strength of Concrete

Fatigue, in the context of materials science and engineering, refers to the weakening or failure of a material caused by repeatedly applied loads, even if these loads are below the strength limit of the material. Fatigue strength in concrete is a critical property that influences its durability and longevity. Concrete can fail in two ways due to fatigue. Static fatigue or creep rupture occurs under a constant load or one that increases slowly. The other failure mode is due to cyclical or...
623