The Present SP Tests for Determining the Transition Temperature T_SP on "U" Notch Disc Specimens

The principal difference between the small punch (SP) testing technique and standardized impact testing lies in the fact that the SP tests carried out in accordance with CWA 15627 Small Punch Test Method for Metallic Materials use disc-shaped test specimens without a notch. Especially in tough materials, the temperature dependence of SP fracture energy E^SP in the transition area is very steep and lies close to the temperature of liquid nitrogen. In this case, the determination of SP transition temperature T_SP can lead to significant errors in its determination. Efforts to move the transition area of penetration testing closer to the transition area of standardized impact tests led to the proposal of the notched disc specimen 8 mm in diameter and 0.5 mm in thickness with a "U" shaped notch 0.2 mm deep in the axis plane of the disc. The paper summarizes the results obtained to date when determining the transition temperature of SP tests T_SP, determined according to CWA 15627 for material of pipes made of P92, P22, and a heat treated 14MoV6-3 steel in the as delivered state. Although the results obtained confirmed the results of other works in that the presence of a notch in a SP disc is insufficient to increase the transition temperature significantly and certainly not to the values obtained by Charpy testing, comparison of the different behaviors of the alloys tested reveals some evidence that the notch reduces the energy for initiation. This implies that the test on a notched disc is more a test of crack growth and would be a useful instrument if included in the forthcoming EU standard for SP testing.