Determination of Aggregate Surface Morphology at the Interfacial Transition Zone ITZ
08:59

Determination of Aggregate Surface Morphology at the Interfacial Transition Zone ITZ

Published on: December 16, 2019

8.8K

SEM Analysis of the Interfacial Transition Zone between Cement-Glass Powder Paste and Aggregate of Mortar under

Yaning Kong1, Peiming Wang2, Shuhua Liu3

  • 1School of Materials Science and Engineering, Tongji University, Shanghai 201804, China. kongyaning1224@126.com.

Materials (Basel, Switzerland)
|August 5, 2017
PubMed

Keywords:
ITZSEMglass powdermicrostructuremicrowave curingmicrowave curing mortarinterfacial transition zone cementglass powder in mortarcement hydration methods

More Related Videos

Sandy Soil Improvement through Microbially Induced Calcite Precipitation MICP by Immersion06:27

Sandy Soil Improvement through Microbially Induced Calcite Precipitation MICP by Immersion

Published on: September 12, 2019

10.2K
Expression of Cementitious Pore Solution and the Analysis of Its Chemical Composition and Resistivity Using X-ray Fluorescence06:27

Expression of Cementitious Pore Solution and the Analysis of Its Chemical Composition and Resistivity Using X-ray Fluorescence

Published on: September 23, 2018

9.8K

Related Concept Videos

Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is...
498
Transition Zone01:28

Transition Zone

The transition zone in concrete is a critical area where aggregate meets cement paste, marked by a distinct porosity and weakness compared to the surrounding material. The adhesion around the aggregates is primarily due to Van Der Waals forces. The voids within this zone influence its robustness; initially, it is less durable than the surrounding bulk mortar due to larger voids. Initially, when concrete is compacted, a higher water-cement ratio near the aggregates leads to the formation of...
430
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
512
Mortar Properties01:17

Mortar Properties

Mortar properties encompass a range of characteristics crucial for construction and masonry work, including workability, water retention, bond strength, durability, compressive strength, volume change, and appearance. Workability refers to mortar's ability to be easily applied and manipulated without sagging or falling off surfaces, which is important for efficient masonry unit placement and alignment. Water retention is essential to prevent the mortar from losing moisture too quickly to...
529
Mortar01:29

Mortar

Mortar, a mixture of Portland cement, hydrated lime, sand, and water, is a crucial binding material in construction. Its primary function is to join masonry units together, filling gaps and ensuring a uniform distribution of weight across the structure. This helps in preventing potential weaknesses. Mortar also serves as a protective barrier against environmental elements such as water and wind, thereby safeguarding the interior of the structure. It also compensates for surface irregularities...
669
Pore Size Distribution01:23

Pore Size Distribution

In concrete, the pore size distribution significantly influences the material's properties. Capillary pores, markedly larger than gel pores, form a vast network within partially hydrated cement paste, reducing the concrete's strength and increasing its permeability. This heightened permeability leads to a greater risk of damage from environmental factors like freeze-thaw cycles and chemical attacks, with the extent of vulnerability also being tied to the water-to-cement ratio.
Adequate...
516