Effect of Stress Ratio and Loading Frequency on the Corrosion Fatigue Behavior of Smooth Steel Wire in Different

Songquan Wang1, Dekun Zhang2, Ningning Hu3

  • 1School of Mechatronic Engineering, Jiangsu Normal University, Xuzhou 221116, China. wbplsz@outlook.com.

Materials (Basel, Switzerland)
|August 5, 2017
PubMed

Keywords:
corrosion fatigueloading frequencysteel wirestress ratio

More Related Videos

Applicability Analysis of Assessment Methods for Morphological Parameters of Corroded Steel Bars10:24

Applicability Analysis of Assessment Methods for Morphological Parameters of Corroded Steel Bars

Published on: November 1, 2018

7.0K
Ultrasonic Fatigue Testing in the Tension-Compression Mode06:54

Ultrasonic Fatigue Testing in the Tension-Compression Mode

Published on: March 7, 2018

11.2K

Related Concept Videos

Fatigue01:21

Fatigue

Fatigue occurs when materials rupture under repeated or fluctuating loads, even at stress levels far below their static breaking strength. It typically results in brittle failure, even for ductile materials. It is a critical consideration in designing machines and structural components subjected to repetitive or varying loads. The nature of these loadings can range from fluctuating loads like unbalanced pump impellers causing vibrations to repeatedly bending a thin steel rod wire back and forth...
888
Stress Concentrations01:24

Stress Concentrations

Stress concentration is when stress intensifies near discontinuities such as holes or abrupt cross-sectional changes in a structural member. This localized stress can often surpass the average stress within the member. The stress distribution in flat bars, either with a circular hole or varying widths connected by fillets, can be determined experimentally using a photoelastic method. The results are based on ratios of geometric parameters like the ratio of the hole's radius to the smaller...
743
Stress Concentrations01:13

Stress Concentrations

The concept of stress concentration is crucial for understanding how materials respond under bending stresses, particularly when there are irregularities or discontinuities in the material's geometry. Normally, stress in a symmetric member subjected to pure bending is assumed to be uniformly distributed across the entire cross-section. However, this assumption does not hold when there are variations in the cross-sectional geometry or the presence of notches and holes.
The stress...
708
Stress-Strain Diagram - Ductile Materials01:24

Stress-Strain Diagram - Ductile Materials

The stress-strain relationship in ductile materials such as structural steel or aluminium is intricate and progresses through several stages. When a specimen is loaded, it initially exhibits a linear length increase, depicted by a steep straight line on the stress-strain diagram. It indicates the material is elastically deforming and will return to its original shape once unloaded. However, when a critical stress value is reached, plastic deformation begins. This stage sees substantial...
2.2K
Stress: General Loading Conditions01:15

Stress: General Loading Conditions

To grasp the intricacy of real-world conditions where multiple loads are applied simultaneously to a structure, one might visualize a section passing through a specific point within a body, aligned parallel to the xy plane. This section is subjected to various forces, including original loads, normal forces, and shearing forces.
The shearing force, possessing potential directionality within the plane of the section, is simplified into two component forces running parallel to the x and y axes....
630
Hooke's Law01:26

Hooke's Law

Hooke's law, a pivotal principle in material science, establishes that the strain a material undergoes is directly proportional to the applied stress, defined by a factor called the modulus of elasticity or Young's modulus.
1.7K