Stress Corrosion Cracking of an Austenitic Stainless Steel in Nitrite-Containing Chloride Solutions

R K Singh Raman1, Wai Hoong Siew2

  • 1Department of Mechanical and Aerospace Engineering, Monash University, Melbourne, Victoria 3800, Australia. raman.singh@monash.edu.

Materials (Basel, Switzerland)
|August 10, 2017
PubMed

Keywords:
austenitic stainless steelchloride stress corrosion cracking

More Related Videos

Full-field Strain Measurements for Microstructurally Small Fatigue Crack Propagation Using Digital Image Correlation Method07:37

Full-field Strain Measurements for Microstructurally Small Fatigue Crack Propagation Using Digital Image Correlation Method

Published on: January 16, 2019

10.2K
Micromechanical Tension Testing of Additively Manufactured 17-4 PH Stainless Steel Specimens05:38

Micromechanical Tension Testing of Additively Manufactured 17-4 PH Stainless Steel Specimens

Published on: April 7, 2021

3.9K

Related Concept Videos

Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
610
2° Amines to N-Nitrosamines: Reaction with NaNO201:20

2° Amines to N-Nitrosamines: Reaction with NaNO2

Secondary amines react with nitrous acid to form N-nitrosamines, as depicted in Figure 1. Nitrous acid, a weak and unstable acid, is formed in situ from an aqueous solution of sodium nitrite and strong acids, such as hydrochloric acid or sulfuric acid, in cold conditions. In the presence of an acid, the nitrous acid gets protonated. The subsequent loss of water results in the formation of the electrophile known as nitrosonium ion.
5.6K
Corrosion02:49

Corrosion

The degradation of metals due to natural electrochemical processes is known as corrosion. Rust formation on iron, tarnishing of silver, and the blue-green patina that develops on copper are examples of corrosion. Corrosion involves the oxidation of metals. Sometimes it is protective, such as the oxidation of copper or aluminum, wherein a protective layer of metal oxide or its derivatives forms on the surface, protecting the underlying metal from further oxidation. In other cases, corrosion is...
28.7K
Precipitation Titration Curve: Analysis01:21

Precipitation Titration Curve: Analysis

The precipitation titration curve demonstrates the change in concentration of one reactant with the volume of titrant added. During the titration of chloride ions with silver nitrate, the precipitation titration curve is divided into three regions: before, at, and after the equivalence point. Before the equivalence point, low redissolution of the sparingly soluble silver chloride precipitate gives a low silver ion concentration. However, in the second region, representing the equivalence point,...
1.9K
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
512
1° Amines to Diazonium or Aryldiazonium Salts: Diazotization with NaNO2 Overview01:26

1° Amines to Diazonium or Aryldiazonium Salts: Diazotization with NaNO2 Overview

Nitrous acid and nitric acids are two types of acids containing nitrogen, among which nitrous acid is weaker than nitric acid. Nitrous acid with a pKa value of 3.37 ionizes in water to give a nitrite ion and the hydronium ion.
The nitrous acid is unstable. Hence, it is formed in situ from a solution of sodium nitrite and cold aqueous acids such as hydrochloric or sulfuric acid. In an acidic solution, the –OH group of nitrous acid undergoes protonation to give oxonium ion, followed by...
4.0K