Collagen cross-linking as an adjunct for repair of corneal lacerations: a cadaveric study
Timothy Ratzlaff1, David Wei2, Yao Wang1
1Department of Ophthalmology, Queen's University, Kingston, Ont.
Objective:
To determine the efficacy of collagen cross-linking (CXL) as an adjunct to suturing in the repair of corneal lacerations.
Methods:
A cadaveric study was undertaken in which a linear 5 mm corneal laceration was created in the central cornea of 20 eyes. The eyes were then randomized to receive 1 (n = 8), 2 (n = 8), or 3 (n = 4) standard corneal sutures. The burst pressure of the wound was then measured. All eyes in the 1- and 2-suture group then underwent standard CXL, with burst pressure repeated afterward.
Results:
The initial wound burst pressure in the 1-, 2-, and 3-suture groups was 54.9, 74.0, and 201.2 mm Hg, respectively. After CXL, wound burst pressure increased by a mean of 3.2 and 62.3 mm Hg in the 1- and 2-suture groups, respectively. This change was statistically significant in the 2-suture group (p = 0.017). After CXL, the 2-suture group still had a significantly lower burst pressure compared with the 3-suture group (p = 0.011).
Conclusions:
The study highlights a potential novel application for CXL to strengthen corneal wounds. Provided that suture density is sufficient to appose the wound edges, CXL may result in short-term wound strengthening. This could potentially allow for decreased corneal suture density and a corresponding decrease in suture-related complications.