Supercritical carbon dioxide decellularised pericardium: Mechanical and structural characterisation for applications
Frank R Halfwerk1, Jeroen Rouwkema2, Jan A Gossen3
1Department of Cardio-Thoracic Surgery, Thoraxcentrum Twente, Medisch Spectrum Twente Hospital, PO Box 50000, 7500 KA Enschede, The Netherlands; Department of Biomechanical Engineering, Faculty of Engineering Technology, University of Twente, PO Box 217, 7500 AE Enschede, The Netherlands.
Introduction:
Many biomaterials are used in cardio-thoracic surgery with good short-term results. However, calcification, dehiscence, and formation of scar tissue are reported. The aim of this research is to characterise decellularised pericardium after supercritical carbon dioxide (scCO2) processing as an alternative biological material for uses in cardio-thoracic surgery.
Methods:
Porcine and bovine pericardium were decellularised using scCO2. Mechanical properties such as tensile strength, elastic modulus, fracture toughness and suture retention strength were determined. Ultrastructure was visualised using Scanning Electron Microscopy. Water uptake and swelling was experimentally determined. Commercially available glutaraldehyde treated bovine pericardium was used as gold standard for comparison.
Results:
scCO2 decellularised porcine (and bovine pericardium) maintained their tensile strength compared to untreated native pericardium (13.3 ± 2.4MPa vs 14.0 ± 4.1MPa, p = 0.73). Tensile strength of glutaraldehyde treated pericardium was significantly higher compared to untreated pericardium (19.4 ± 7.3MPa vs 10.2 ± 2.2MPa, p = 0.02). Suture retention strength of scCO2 treated pericardium was significantly higher than glutaraldehyde treated pericardium (p = 0.01). We found no anisotropy of scCO2 or glutaraldehyde treated pericardium based on a trouser tear test. Ultrastructure was uncompromised in scCO2 treated pericardium, while glutaraldehyde treated pericardium showed deterioration of extracellular matrix.
Conclusion:
scCO2 processing preserves initial mechanical and structural properties of porcine and bovine pericardium, while glutaraldehyde processing damages the extracellular matrix of bovine pericardium. Decellularisation of tissue using scCO2 might give long-term solutions for cardio-thoracic surgery without compromising initial good mechanical properties.