Nitrogen-Rich Conjugated Microporous Polymers: Facile Synthesis, Efficient Gas Storage, and Heterogeneous Catalysis

Nitrogen-rich conjugated microporous polymers (NCMPs) have attracted great attention in recent years owing to their polarity, basicity, and ability to coordinate metal ions. Herein, three NCMPs, structurally close to polyaniline, were facilely synthesized via chemical oxidative polymerization between multiconnected aniline precursors. The NCMPs with high N content (11.84 wt %), intrinsic ultramicroporosity (<1 nm), and moderate surface area (485 m² g^-1) show wide-ranging adsorption functionality, e.g., CO₂ uptake (11 wt %) and CO₂-selectivity over N₂ (360, 1 bar), 1.0 wt % H₂ storage, as well as 215 wt % iodine vapor uptake at ambient pressure. Moreover, these NCMPs act as support for palladium catalysts and can maintain >94% activity in Suzuki-Miyaura coupling reactions after six continuous runs.