Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
Impact of Root Dentin Thickness on the in vitro Compressive Strength of Teeth treated with Recent Post and Core
Amit Bhagat1, Litik Mittal2, Sahil Mogla3
1Department of Conservative Dentistry and Endodontics National Dental College and Hospital, Dera Bassi, Punjab, India, Phone: +919501544877
Introduction:
Endodontically treated teeth dry with time, and its dentin undergoes changes making the teeth brittle and friable. The main function of a post is to strengthen or reinforce a weakened root. However, doing a post and core frequently requires the removal of sound tooth tissue. Recent materials introduced in the market for post and cores have been promising.
Aim:
The aim of this study is to evaluate the fracture resistance of endodontically treated extracted permanent teeth with variable remaining root dentin thickness after post space preparation.
Materials And Methods:
A total of 270 freshly extracted permanent maxillary central incisors with fully formed apices were selected, decoronated at cementoenamel junction, and divided into three main groups according to remaining root dentin thickness, determined using a Vernier caliper into 0.5, 1, and 1.50 mm after post space preparation. Each group was further divided into three subgroups (subgroup a: Custom-made cobalt-chromium alloy post and core; subgroup b: Prefabricated glass fiber post and composite core; and subgroup c: EverStick fiber post). Each specimen was subjected to compressive load using universal testing machine. The force required to fracture was recorded and data were analyzed using analysis of variance (ANOVA) test.
Results:
Analysis of variance revealed that compressive strength of the tooth is significantly affected by the increase in the remaining dentin thickness after post space preparation (p < 0.05). Furthermore, teeth with custom fabricated posts showed a significantly higher compressive strength (p < 0.05) than prefabricated glass fiber post and EverStick fiber post groups except the group with minimum remaining dentin thickness.
Conclusion:
The present in vitro study revealed that compressive strength of the post and core systems is directly related to the amount of healthy remaining dentin thickness. Hence, efforts to maximize the preservation of natural dentin should be taken during post space preparation.
Related Concept Videos
01:21Tooth Anatomy
The Crown, Neck, and Root
The visible part of the tooth is referred to as the crown. It's covered by enamel, the hardest substance in the human body. The crown is uniquely shaped for each type of tooth, allowing for different functions such as cutting, tearing, or...
01:30Relation Between Tensile Strength and Compressive Strength of Concrete
01:21Impact Strength of Concrete
01:16Tensile Strength Considerations of Concrete
The dimensions and shape of a concrete specimen...
01:18Porosity in Cement Paste
The balance of water to cement in the mix is...
01:23Behavior of Concrete Under Compressive Load
As the concrete specimen fractures under...