Synthesis of thiolated arabinoxylan and its application as sustained release mucoadhesive film former

The present work aimed to synthesize thiolated arabinoxylan (TAX), and to evaluate its mucoadhesive potential. Synthesis of TAX was accomplished by esterification of arabinoxylan (AX) with thioglycolic acid (TGA). The appearance of a characteristic peak at 2516 cm^-1 in the FTIR spectrum of TAX, and presence of 6.01 ± 1.03 m moles of thiol per gram of the polymer confirmed successful thiolation of AX. The incorporation of the thiol group considerably promoted mucoadhesive strength of the polymer-viz. 3.99-fold. Moreover, in vivo safety analysis in albino rats revealed TAX to be safe in the concentration range of 750-1000 mg kg^-1 body weight. Synthesized TAX was utilized to prepare Tizanidine HCl (TZN HCl) loaded sustained release (SR) mucoadhesive buccal films using a solvent casting technique. Results proved that the prepared films were of uniform thickness, good mechanical strength (with folding endurance >300), acceptable moisture contents (5%-7%) and surface pH (6.23 ± 0.81 to 6.43 ± 0.49) compatible to that of the buccal cavity. Presence of greater that 90% of drug contents indicated the excellent drug loading ability of the prepared films. Results of in vitro dissolution studies and ex vivo permeation studies conducted respectively by USP dissolution apparatus II and Franz diffusion cell indicated that sustained effect of TAX was achieved for 8 h. These results have conclusively proven that TAX has the potential to improve the bioavailability of TZN HCl due to enhanced mucoadhesion in buccal cavity, hence signifying its suitability as a mucoadhesive buccal film former.