Relative Translucency of a Multilayered Ultratranslucent Zirconia Material
Loubna Shamseddine1, Zeina Majzoub2
1Department of Prosthodontics, Lebanese University, School of Dentistry, Beirut, Lebanon, Phone: +96170916424,
Aim:
The aim of this study was to compare the translucency parameter (TP) of ultratranslucent multilayered (UTML) zirconia according to thickness and layer level.
Materials And Methods:
Rectangles of UTML zirconia with four layers [dentin layer (DEL), first transitional layer (FTL), second transitional layer (STL), and enamel layer (ENL)] and four different thicknesses (0.4, 0.6, 0.8, and 1 mm) were milled from blanks. Digital images were taken in a dark studio against white and black backgrounds under simulated daylight illumination and international commission on illumination (CIE) Lab* color values recorded using Photoshop Creative Cloud software. The TP was computed and compared according to thickness and layer level using analysis of variance (ANOVA) followed by Bonferroni post hoc analysis for multiple comparisons. Significance was set at p < 0.05.
Results:
In each thickness, TP values were similar between any two layers. The significant effect of thickness on the TP was observed only in the first two layers. In the DEL, translucency was significantly greater at 0.4 mm than all other thicknesses. In the FTL, differences were significant between 0.4 and 0.8 mm and between 0.4 and 1 mm.
Conclusion:
The investigated zirconia does not seem to show gradational changes in relative translucency from dentin to enamel levels regardless of the thickness used. Thickness affected the TP only in the first two layers with better translu-cency at 0.4 mm.
Clinical Significance:
Since relative translucency does not seem to be significantly different between layers, clinicians can modify the apicocoronal positioning of the UTML layers within the restoration according to the desired Chroma without any implications on the clinically perceived translucency. While the thickness of 0.4 mm may be suggested for anterior esthetic veneers because of its higher translucency, the other thicknesses of 0.6 to 1 mm can be used to mask colored abutments in full contour restorations.