Novel MOF-Derived Co@N-C Bifunctional Catalysts for Highly Efficient Zn-Air Batteries and Water Splitting

Metal-organic frameworks (MOFs) and MOF-derived materials have recently attracted considerable interest as alternatives to noble-metal electrocatalysts. Herein, the rational design and synthesis of a new class of Co@N-C materials (C-MOF-C2-T) from a pair of enantiotopic chiral 3D MOFs by pyrolysis at temperature T is reported. The newly developed C-MOF-C2-900 with a unique 3D hierarchical rodlike structure, consisting of homogeneously distributed cobalt nanoparticles encapsulated by partially graphitized N-doped carbon rings along the rod length, exhibits higher electrocatalytic activities for oxygen reduction and oxygen evolution reactions (ORR and OER) than that of commercial Pt/C and RuO₂ , respectively. Primary Zn-air batteries based on C-MOF-900 for the oxygen reduction reaction (ORR) operated at a discharge potential of 1.30 V with a specific capacity of 741 mA h g_Zn^-1 under 10 mA cm^-2 . Rechargeable Zn-air batteries based on C-MOF-C2-900 as an ORR and OER bifunctional catalyst exhibit initial charge and discharge potentials at 1.81 and 1.28 V (2 mA cm^-2 ), along with an excellent cycling stability with no increase in polarization even after 120 h - outperform their counterparts based on noble-metal-based air electrodes. The resultant rechargeable Zn-air batteries are used to efficiently power electrochemical water-splitting systems, demonstrating promising potential as integrated green energy systems for practical applications.