Photopolymerized maleilated chitosan/thiol-terminated poly (vinyl alcohol) hydrogels as potential tissue engineering...

Photocrosslinkable hydrogels composed of natural materials exhibit great application potential in tissue engineering scaffolds. However, weak formation and poor mechanical property can usually be a limitation. Herein, the photo-clickable thiol-ene hydrogels based chitosan were synthesized using photopolymerization of maleic chitosan (MCS) and thiol-terminated poly (vinyl alcohol) (TPVA) in the presence of a biocompatible photoinitiator. Rheological property and absorbing behavior of the MCS/TPVA hydrogels could be tailored by varying the amount of TPVA in the feed. There was strong intermolecular hydrogen bonding between the molecules of MCS and TPVA. Notably, the MCS/TPVA hydrogel (MT-3) exhibited rapid gelation behavior (<120 s), improved stiff (G' = ∼5500 Pa) and compressive strength (0.285 ± 0.014 MPa), which were important for hydrogel scaffolds, especially for injectable hydrogel scaffolds. Photocrosslinked MCS/TPVA hydrogels was cytocompatible and could promote the L929 cells attachment and proliferation, showing their potential as tissue engineering scaffolds.