Influence of cleaning methods on resin bonding to saliva-contaminated zirconia

The aim of this study was to investigate the influence of different cleaning methods on the shear bond strengths of 2 resin cements to saliva-contaminated zirconia.

After saliva contamination, alumina-blasted zirconia specimens were cleaned with 1 of 5 methods of water-rinsing (SA), K-etchant GEL phosphoric acid (PA), Ivoclean (IC), AD Gel (ADG), or additional alumina-blasting (AB). Alumina-blasted zirconia without saliva contamination was used as control group (Cont). Composite cylinders were bonded to the zirconia with 1 of 2 dual-cured resin cements. The bond strengths were measured by shear testing after 24 hours (TC0) and after thermal cycling at 4°C-60°C (TC10 000) and specimen surfaces were evaluated using X-ray photoelectron spectroscopy (XPS). Data were statistically analyzed using 3-way analysis of variance and Tukey test (α = 0.05).

There were no significant differences in the bond strengths of 2 resin cements between the Cont ADG, and AB groups before and after TCs (P > .05). SA, PA, and IC groups did not exhibit durable resin bonding to zirconia. XPS showed that carbon and nitrogen increased in the SA group in comparison to the Cont group. The concentration of carbon in other 4 groups returned to the concentration range of the Cont group; however, nitrogen was not detected in the only AB group.

Saliva contamination significantly reduced the bond strength of 2 resin cements to zirconia. Additional AB or cleaning with ADG resulted in effective cleaning of saliva contamination and preserved resin cement bond strength to zirconia.

Saliva contamination occurs during clinical procedures for adjustment of zirconia ceramic restorations in the oral environment. AD Gel application is effective for removing saliva contaminants on the alumina-blasted zirconia surface beforehand by the dental laboratory instead of additional AB since AD Gel application and AB had a similar effect on the removal of organic components of saliva.