An Asymmetric Supercapacitor Based on Activated Porous Carbon Derived from Walnut Shells and NiCo₂O₄ Nanoneedle Arrays Electrodes

A facile method was utilized to convert a common biomass of walnut shells into activated porous carbon by carbonization and activation with nitricacid treatment. The obtained activated carbon (WSs-2) exhibited excellent electrochemical performance with high specific capacitance of 137 F · g-1 at 1 A · g-1 and super cycling performance of 96% capacitance retention at 5 A · g-1 after 5000 cycles. In addition, NiCo2O4 nanoneedle arrays with good electrochemical properties were successfully prepared by a simple hydrothermal method. An aqueous asymmetric supercapacitor (ASC) device based on WSs-2 and NiCo2O4 was assembled, which delivered 21 Wh · kg-1 at a power density of 424.5 W · kg-1, and maintained 19 Wh · kg-1 at power density of 4254 W · kg-1 as well as excellent cycling stability of 99.3% capacitance retention after 5000 cycles at 4 A · g-1. Through this method, low-cost, environmentally friendly and large-scale carbon materials can be fabricated and applied in supercapacitor electrodes.