Wear and Corrosion Interactions at the Titanium/Zirconia Interface: Dental Implant Application

Dental implants have been shown to have predictable success, but esthetic complications often arise. To reduce tissue shadowing from titanium, zirconia abutments may be used; however, the literature suggests that the use of zirconia leads to greater destruction of the implant interface that may result in biological complications such as titanium tattoos and heavy metal toxicity. Previous studies have examined the mechanical aspects of this implant/abutment relationship, but they have not accounted for the corrosive degradation that also takes place in the dynamic environment of the oral cavity. This study investigated the combined effect of both wear and corrosion on the materials at the implant and abutment interface.

Using a simulated oral tribocorrosive environment, titanium (Ti) and zirconia (Zr) abutment materials were slid against titanium and Roxolid implant alloys. The four couplings (Ti/Ti, Ti/Rox, Zr/Ti, Zr/Rox) were selected for the tribocorrosion tests (N = 3). The testing was conducted for 25K cycles, and the coefficient of friction (CoF) and voltage evolution were recorded simultaneously. Following the tribocorrosion assays, the wear volume loss was calculated, and surface characterization was performed. Statistical analysis was completed using a one-way ANOVA followed by post-hoc Bonferroni comparisons.

Zr/Ti groups had the highest CoF (1.1647), and Ti/Ti had the lowest (0.5033). The Zr/Ti coupling generated significantly more mechanical damage than the Ti/Ti group (p = 0.021). From the corrosion aspect, the Ti/Ti groups had the highest voltage drop (0.802 V), indicating greater corrosion susceptibility. In comparison, the Zr/Roxolid group had the lowest voltage drop (0.628 V) and significantly less electrochemical degradation (p = 0.019). Overall, the Ti/Ti group had the largest wear volume loss (15.1 × 10⁷ μm³ ), while the Zr/Ti group had the least volume loss (2.26 × 10⁷ μm³ ). Both zirconia couplings had significantly less wear volume than the titanium couplings (p < 0.001).

This study highlights the synergistic interaction between wear and corrosion, which occurs when masticatory forces combine with the salivary environment of the oral cavity. Overall, the zirconia groups outperformed the titanium groups. In fact, the titanium groups generated 5 to 6 times more wear to the implant alloys as compared with the zirconia counterparts. The best performing group was Zr/Ti, and the worst performing group was Ti/Ti.