Nanosized Hydroxyapatite Precipitation on the Ti—30Ta—xHf Alloys

In this study, we prepared hydroxyapatite (HAp) layer on the alkali treated Ti–30Ta–xHf alloys using electrochemical deposition method. Ti–30Ta–xHf alloys was anodized in 5 M NaOH solution at 0.3 A for 10 min. Alkali treated Ti–30Ta–xHf surface formed by anodization step which acted as templates and anchorage for growth of the HAp during subsequent pulsed electrochemical deposition process at 85 °C. The phase and morphologies of deposited HAp layer were affected by the Hf contents of Ti–30Ta–xHf alloys. The nano-scale rod-like HAp layer was formed on untreated Ti–30Ta–xHf alloys with partially low crystallinity. In the case of alkali treated Ti–30Ta–xHf, nano-sized needle-like layers were transferred to nano-flake surface and denser morphology as Hf content increased.