A Novel Fabrication Method of Bi₂Te₃-Based Thermoelectric Modules by Indium Electroplating and Thermocompression...

In this study, we devised a method to bond thermoelectric elements directly to copper electrodes by plating indium with a relatively low melting point. A coating of indium, ~30 μm in thickness, was fabricated by electroplating the surface of a Bi2Te3-based thermoelectric element with a nickel diffusion barrier layer. They were then subjected to direct thermocompression bonding at 453 K on a hotplate for 10 min at a pressure of 1.1 kPa. Scanning electron microscopy images confirmed that a uniform bond was formed at the copper electrode/thermoelectric element interface, and the melted/solidified indium layer was defect free. Thus, the proposed novel method of fabricating a thermoelectric module by electroplating indium on the surface of the thermoelectric element and directly bonding with the copper electrode can be used to obtain a uniformly bonded interface even at a relatively low temperature without the use of solder pastes.