In Vitro Evaluation of The Effects Of Er,Cr:YSGG and Diode Lasers Used on Titanium Cylinder
Published on: June 6, 2025
Effect of Er,Cr:YSGG Laser and Ascorbic Acid on the Bond Strength and Microleakage of Bleached Enamel Surface
Fahad Alkhudhairy1, Abdulaziz AlKheraif2, Mohammed Bin-Shuwaish1
11 Department of Restorative Dental Sciences, College of Dentistry, King Saud University , Riyadh, Saudi Arabia .
Background:
The available evidence of Er,Cr:YSGG lasers on bleached enamel is limited and controversial. It is assumed that Er,Cr:YSGG laser will be effective in reversing the effect of bleaching on adhesive bond integrity of enamel to resin composite.
Objective:
The study aimed to evaluate the efficacy of Er,Cr:YSGG laser on bond strength and microleakage of bleached enamel.
Materials And Methods:
From the 80 samples, 60 samples were bleached (40% hydrogen peroxide) and divided into three subgroups. Twenty bleached samples in each subgroup were exposed to 10% sodium ascorbate (Gp A), Er,Cr:YSGG laser (50 Hz and 4.5 W) (Gp L), and no treatment (Gp B), respectively. Twenty samples were not bleached (Control-C). Using etch and rinse technique, resin composite was built-up on enamel and photopolymerized. Ten specimens in each group were tested for shear bond strength at a crosshead speed of 1 mm/min. Ten specimens in each group were tested for microleakage using 2% methylene blue. Data were analyzed using analysis of variance (ANOVA) and Tukey post hoc multiple comparisons test.
Results:
The mean bond strength of specimens in group L (30.83 ± 1.7000) was comparable with group A (31.38 ± 2.03) and was significantly higher than bleached specimens (9.49 ± 0.86) (p < 0.001). The highest mean microleakage values were observed in bleached group (630.32 ± 156.58). The mean microleakage among control (36.66 ± 27.33) and laser group specimens (55.32 ± 34.98) was comparable (p > 0.05).
Conclusions:
Treatment of bleached enamel with erbium, chromium:yttrium-scandium-gallium-garnet (Er,Cr:YSGG) laser showed a significant reversal effect on the enamel bond strength and microleakage scores.
Clinical Significance:
Er,Cr:YSGG laser (50 Hz, 4.5 W) treatment has the potential to restore the bond strength of bleached enamel to resin composite.
More Related Videos
Related Concept Videos
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
01:12Bonding and Strength of Aggregate
03:38Polyprotic Acids
02:29Relative Strengths of Conjugate Acid-Base Pairs
02:35Acid and Bases: Ka, pKa, and Relative Strengths
00:42Ionic Bonds
When atoms gain or lose electrons to achieve a more stable electron configuration they form ions. Ionic bonds are electrostatic attractions between ions with opposite charges. Ionic compounds are rigid and brittle when solid and may dissociate into their constituent ions in water. Covalent compounds, by contrast, remain intact unless a chemical reaction breaks them.
Opposing Charges Hold Ions Together in Ionic Compounds
Ionic bonds are reversible electrostatic interactions between ions...