Osteogenesis of 3D printed porous Ti6Al4V implants with different pore sizes

Selective laser melting (SLM) is one of the three-dimensional (3D) printing techniques that manufacturing versatile porous scaffolds with precise architectures for potential orthopedic application. To understand how the pore sizes of porous Ti6Al4V scaffolds affect their biological performances, we designed and fabricated porous Ti6Al4V implants with straightforward pore dimensions (500, 700, and 900 µm) via SLM, termed as p500, p700, and p900 respectively. The morphological characteristics of Ti6Al4V scaffolds were assessed showing that the actual pore sizes of these scaffolds were 401 ± 26 µm, 607 ± 24 µm, 801 ± 33 µm, respectively. The mechanical properties of Ti6Al4V scaffolds were also evaluated showing that they were comparable to that of bone tissues. Meanwhile, the effect of pore size on biological responses was systematically investigated in vitro and in vivo. It was verified that 3D printing technique was able to fabricate porous Ti6Al4V implants with proper mechanical properties analogous to human bone. The in vitro results revealed that scaffolds with appropriate pore dimension were conducive to cell adhesion, proliferation and early differentiation. Furthermore, the porous Ti6Al4V scaffolds were implanted into the rabbit femur to investigate bone regeneration performance, the in vivo experiment showed the p700 sample was in favor of bone ingrowth into implant pores and bone-implant fixation stability. Taken together, the biological performance of p700 group with actual pore size of about 600 µm was superior to other two groups. The obtained findings provide basis to individually design and fabricate suitable porous Ti6Al4V with specific geometries for orthopedic application.