Effect of ceramic thickness and cement shade on the final shade after bonding using the 3D master system: a...

The final color of a ceramic restoration is influenced by both the ceramic thickness and the cement shade. This study aims to evaluate the color stability according to the 3D Master System of e.max ceramic discs after bonding with different shades of luting agents. A total of 120 e.max.Press 2M1 HT ceramic discs (60 discs of 1-mm thick and 60 discs of 0.5 mm thick) and three different values of Variolink Veneer cement were used (-3, 0, +3) for the cementation process. An Easyshade compact device was used to measure color shade tabs, according to the 3D Master System, on the discs both before and after the cementation protocols. Bivariate and multivariate analyses were carried out with the spss v.21. After bonding with the different luting agents, only 30% remained as 2M1: specifically, 22% of the thinner discs and 37.3% of the thicker discs. In general, the effect of bonding increased the value and the chroma of the shade to a significant extent. Regression analyses revealed that the most significant predictor for all color parameters was cement shade, the thinner disc group bonded with -3 cement being the most unstable subgroup. According to the 3D Master System, the shade of the luting agent was the main predictor of the final color. However, the final color seems to be somewhat unpredictable, at least according to the modulating factors evaluated in the present study.