Cetyltrimethylammonium bromide intercalated and branched polyhydroxystyrene functionalized montmorillonite clay to...

Herein, Cetyltrimethyl ammonium bromide (CTAB) intercalated and branched polyhydroxystyrene (BPS) functionalized montmorillonite (MMT) nano-composite (BPS-CTAB-MMT) was developed, characterized, and its potential as an adsorbent was tested in sequestering cationic dyes viz. rhodamine B (RB), crystal violet (CV), and methylene blue (MB) from aqueous environment. N₂ adsorption/desorption isotherm showed mesoporous BPS-CTAB-MMT surface with a BET surface area of 273.8 m²/g. The appearance of sharp spikes at 2855 and 2925 cm^-1 (associated with symmetric and asymmetric tensions of C - H bonds) in infra-red spectrum of BPS-CTAB-MMT indicates successful intercalation of MMT with CTAB and functionalization with BPS. The observed crystallite size of BPS-CTAB-MMT was 66 nm. Comparatively greater weight loss for BPS-CTAB-MMT (11%) than MMT (9%) was observed during thermogravimetric analysis. The adsorption of dyes on BPS-CTAB-MMT was pH dependent with maximum uptake was observed in the pH range: 5-6. For initial dyes concentration (C_o) range: 50-150 mg/L, the observed equilibration time for CV was 300 min, whereas for RB and MB the equilibration time varied between 300 and 360 min. Modeling investigations revealed the applicability of Sips isotherm and pseudo-second-order (PSO) kinetic models to dyes adsorption data. Sips maximum adsorption capacity (q_s) values for RB, CV, and MB at 55 °C were 476.5, 438.7, and 432.7 mg/g, respectively. The adsorption of dyes on BPS-CTAB-MMT was thermodynamically favorable. Desorption studies showed 42.1% RB and 41.9% CV recovery with 0.1 M NaOH and CH₃COCH₃, respectively, while only traces of MB were recovered with tested eluents.