Microstructure Evolution and Mechanical Behavior of 2219 Aluminum Alloys Additively Fabricated by the Cold Metal
Xuewei Fang1,2, Lijuan Zhang3, Hui Li4
1School of Mechanical Engineering, Xi'an Jiaotong Univeristy, No. 28, Xianning West Road, Xi'an 710049, China. fangxuewei0801@163.com.
Abstract:
In this research, four different welding arc modes including conventional cold metal transfer (CMT), CMT-Pulse (CMT-P), CMT-Advanced (CMT-ADV), and CMT pulse advanced (CMT-PADV) were used to deposit 2219-Al wire. The effects of different arc modes on porosity, pore size distribution, microstructure evolution, and mechanical properties were thoroughly investigated. The statistical analysis of the porosity and its size distribution indicated that the CMT-PADV process gave the smallest pore area percentage and pore aspect ratio, and had almost no larger pores. The results from optical microscopy, scanning electron microscopy, and fractographic morphology proved that uniform and fine equiaxed grains, evenly distributed Al₂Cu second phase particles were formed during the CMT-PADV process. Furthermore, the X-ray diffraction test ascertained that the CMT-PADV sample had the smallest lattice parameter and the highest solute Cu content. Besides, the tensile strength could reach 283 MPa, the data scattering was the smallest, and the strength scattering of the sample in the horizontal direction was the shortest. In addition, the strength properties were nearly isotropic, with only 5 MPa difference in the vertical and horizontal directions. The above mentioned results indicated that the mechanical properties of 2219 aluminum alloy was improved using the CMT-PADV arc mode.
Related Concept Videos
Nucleophilic Addition to the Carbonyl Group: General Mechanism
A stronger nucleophile can directly attack the electrophilic center, the carbonyl carbon. The HOMO orbital of the nucleophile interacts with the LUMO (π* antibonding) orbital present on the carbonyl carbon. This interaction breaks the π bond and shifts the π...
Mechanisms of Heat Transfer
Conduction, accounting for approximately 3% of body heat loss at rest, is the process of exchanging heat between molecules of two materials in direct contact. This can result in both heat loss and gain. For instance, when the body is submerged in water, which conducts heat 20 times more effectively than air, it can either lose or gain significant...
The Evidence for Evolution
Mechanism of heat transfer
Mechanisms of Heat Transfer I
Mechanisms of Heat Transfer II