Wide-band 'black silicon' with atomic layer deposited NbN

Antireflection surfaces are often utilized in optical components to reduce undesired reflection and increase absorption. We report on black silicon (b-Si) with dramatically enhanced absorption over a broad wavelength range (250-2500 nm) achieved by applying a 10-15 nm conformal coating of NbN with atomic layer deposition (ALD). The improvement is especially pronounced in the near infrared (NIR) range of 1100-2500 nm where absorption is increased by >90%. A significant increase of absorption is also observed over the ultraviolet range of 200-400 nm. Preceding NbN deposition with a nanostructured ALD Al₂O₃ (n-Al₂O₃) coating to enhance the NbN texture was also examined. Such texturing further improves absorption in the NIR, especially at longer wavelengths, strong absorption up to 4-5 μm wavelengths has been attested. For comparison, double side polished silicon and sapphire coated with 10 nm thick NbN exhibited absorption of only ∼55% in the NIR range of 1100-2500 nm. The results suggest a positive correlation between the surface area of NbN coating and optical absorption. Based on the wide-band absorption, the presented NbN-coated b-Si may be an attractive candidate for use in e.g. spectroscopic systems, infrared microbolometers.