The Influence of Thermocycling on the Flexural Strength of a Polyamide Denture Base Material
Nick Polychronakis1, Aspasia Sarafianou2, Alcibiadis Zissis1
1Removable Prosthodontics, Dental School, National and Kapodistrian University of Athens, Greece.
Objective:
The aim of the present study was to evaluate the influence of thermocycling on the flexural strength of a polyamide base denture material.
Materials And Methods:
A polyamide denture base material (Valplast) was tested, whereas a PMMA material (Vertex) was used as a control. Thirty specimens of each material were fabricated for flexural strength testing according to ISO 1567. They were prepared and stored in water at 37°C for 48 hours. The specimens of each material were divided into three equal groups (n=10). Flexural strength testing was performed immediately after water storage and after thermocycling (5°C / 55°C, 2 c/min) for 3000 and 5000 cycles. A three point flexural test was performed on a universal testing machine at a crosshead speed of 5 mm/min. The final flexural strength was calculated using the formula: FS = 3 PL/2 bd2. A two-way ANOVA with post-hoc analysis using Tukey's procedure was applied at .05 level of statistical significance.
Results:
A statistically significant reduction in flexural strength was recorded after thermocycling at 3000 cycles for PMMA and at 5000 cycles for both materials. The flexural strength of PMMA was significantly higher compared to polyamide for all the conditions tested (p<0.05).
Conclusion:
Thermocycling had a significant adverse effect on the flexural strength of polyamide and PMMA denture base materials.
Related Concept Videos
02:29Relative Strengths of Conjugate Acid-Base Pairs
01:16Flexural Stress
Hooke's Law states that within the material's elastic limits, stress is directly proportional to strain. In a member experiencing a bending moment, the strain at any point is relative to its distance...
02:35Acid and Bases: Ka, pKa, and Relative Strengths
03:02Acid/Base Strengths and Dissociation Constants
03:05Acid Strength and Molecular Structure
In the absence of any leveling effect, the acid strength of binary compounds of hydrogen with nonmetals (A) increases as the H-A bond strength decreases down a group in the periodic table. For group 17, the order of increasing acidity is HF < HCl < HBr < HI. Likewise, for group 16, the order of increasing acid strength is H2O < H2S < H2Se < H2Te. Across a row in the periodic table, the acid strength of binary hydrogen compounds increases with increasing...
01:20Strength of Cement
For compressive strength tests, ASTM C 109-05 standards prescribe a cement-sand mix ratio of 1:2.75 and a water/cement ratio of 0.485 for making 2-inch cubes. These cubes are mixed, cast, and cured in saturated lime water at 23°C until testing. Flexural strength testing, outlined in...